C13150
| Elements | |
|---|---|
| Cu(1) | |
|
(1) Cu value includes Ag. |
|
| Min (%) | 99.5 |
| Max (%) | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||
| Flat Products | 1/2 Hard | H02 |
37 Min |
| 1/4 Hard | H01 |
34 Min |
|
| 1/8 Hard | H00 |
32 Min |
|
| 3/4 Hard | H03 |
41 Min |
|
| Hard | H04 |
43 Min |
|
| Soft Anneal | O60 |
30 Min |
|
| Melting Point - Liquidus°F | 1981 |
|---|---|
| Melting Point - Solidus°F | 1949 |
| Densitylb/cu in. at 68°F | 0.321 |
| Specific Gravity | 8.9 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 202 |
| Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 9.3 |
| Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 9.6 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.8 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 17400 |
| Modulus of Rigidityksi | 6400 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Fair |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Excellent |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.