C14750
Elements | ||||
---|---|---|---|---|
Cu(1,2) | P | Mn | S | |
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.8% min. |
||||
Min (%) | 0.05 | 0.20 | ||
Max (%) | Rem | 0.012 | 0.50 | 0.50 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Rod, Tubing & Shapes | Hard | H04 |
32 Min 36 Typ 52 Max |
7 Min 29 Typ |
10 Typ |
62.5 Typ |
Wire | Hard | H04 |
32 Min 36 Typ 52 Max |
7 Min 29 Typ |
10 Typ |
62.5 Typ |
Melting Point - Liquidus°F | 1972 |
---|---|
Melting Point - Solidus°F | 1950 |
Densitylb/cu in. at 68°F | 0.321 |
Specific Gravity | 8.9 |
Electrical Conductivity% IACS at 68°F | 0 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 208 |
Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 9.3 |
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 9.5 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.8 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 90 |
Modulus of Elasticity in Tensionksi | 17400 |
Modulus of Rigidityksi | 5950 |
Magnetic Permeability | 1 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Poor |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Poor |
Spot Weld | Poor |
Seam Weld | Poor |
Butt Weld | Fair |
Capacity for Being Cold Worked | Fair |
Capacity for Being Hot Formed | Good |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Solution Treatment | 440 | 530 | ||
Annealing | 750 | 1125 | ||
Hot Working Temperature | 1400 | 1600 |
Typical Uses
Applicable Specifications
Corrosion Properties