C15750
Elements | |||||
---|---|---|---|---|---|
Cu(1) | Fe | Al(2) | B | O(3) | |
(1) Cu value includes Ag. (2) All aluminum present as Al2O3; 0.04% oxygen present as Cu2O with a negligible amount in solid solution with copper. (3) All aluminum present as Al2O3; 0.04% oxygen present as Cu2O with a negligible amount in solid solution with copper. |
|||||
Min (%) | 98.56 | 0.42 | 0.52 | ||
Max (%) | 0.04 | 0.50 | 0.22 | 0.68 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Rod & Bar | As Hot Extruded | M30 |
65 Min 70 Typ 75 Max |
52 Min 55 Typ |
15 Min 20 Max |
75 Min 80 Max |
Melting Point - Liquidus°F | 1981 |
---|---|
Densitylb/cu in. at 68°F | 0.312 |
Specific Gravity | 8.65 |
Technique | Suitability |
---|---|
Soldering | Good |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Poor |
Seam Weld | Poor |
Butt Weld | Poor |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Poor |
Common Fabrication Processes
Thermal Properties
Typical Uses
Applicable Specifications
Corrosion Properties