C15780
| Elements | |||||
|---|---|---|---|---|---|
| Cu(1) | Fe | Al(2) | B | O(3) | |
|
(1) Cu value includes Ag. (2) All aluminum present as Al2O3; 0.04% oxygen present as Cu2O with a negligible amount in solid solution with copper. (3) All aluminum present as Al2O3; 0.04% oxygen present as Cu2O with a negligible amount in solid solution with copper. |
|||||
| Min (%) | 98.10 | 0.66 | 0.76 | ||
| Max (%) | 0.04 | 0.74 | 0.22 | 0.90 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Rod & Bar | As Hot Extruded | M30 |
68 Min 73 Typ 78 Max |
55 Min 58 Typ 61 Max |
8 Min 12 Max |
150 Min 165 Max |
| Melting Point - Liquidus°F | 1976 |
|---|---|
| Densitylb/cu in. at 68°F | 0.038 |
| Specific Gravity | 8.55 |
| Electrical Conductivity% IACS at 68°F | 76 |
| Technique | Suitability |
|---|---|
| Soldering | Good |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Poor |
| Seam Weld | Poor |
| Butt Weld | Poor |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Poor |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.