C15790
| Elements | |||||
|---|---|---|---|---|---|
| Cu(1) | Fe | Al(2) | B | O(3) | |
|
(1) Cu value includes Ag. (2) All aluminum present as Al2O3; 0.04% oxygen present as Cu2O with a negligible amount in solid solution with copper. (3) All aluminum present as Al2O3; 0.04% oxygen present as Cu2O with a negligible amount in solid solution with copper. |
|||||
| Min (%) | 97.68 | 0.88 | 0.96 | ||
| Max (%) | 0.04 | 0.96 | 0.22 | 1.10 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Rod & Bar | As Hot Extruded | M30 |
71 Min 77 Typ 83 Max |
58 Min 61 Typ 64 Max |
7 Min 11 Max |
175 Min 195 Max |
| Melting Point - Liquidus°F | 1976 |
|---|---|
| Densitylb/cu in. at 68°F | 0.307 |
| Specific Gravity | 8.51 |
| Electrical Conductivity% IACS at 68°F | 69 |
| Technique | Suitability |
|---|---|
| Soldering | Good |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Poor |
| Seam Weld | Poor |
| Butt Weld | Poor |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Poor |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.