C15900
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1) | Fe | Al(2) | C | O(3) | Ti | |
(1) Cu value includes Ag. (2) All aluminum present as Al2O3; 0.04% oxygen present as Cu2O with a negligible amount in solid solution with copper. (3) All aluminum present as Al2O3; 0.04% oxygen present as Cu2O with a negligible amount in solid solution with copper. |
||||||
Min (%) | 97.51 | 0.76 | 0.27 | 0.40 | 0.66 | |
Max (%) | 0.04 | 0.84 | 0.33 | 0.54 | 0.74 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
Elongation (%) |
Rockwell B scale |
---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||
Rod & Bar | As Hot Extruded | M30 |
100 Min 104 Typ 109 Max |
5 Min 8 Max |
93 Min 97 Max |
Melting Point - Liquidus°F | 1981 |
---|---|
Densitylb/cu in. at 68°F | 0.318 |
Specific Gravity | 8.84 |
Electrical Conductivity% IACS at 68°F | 48 |
Technique | Suitability |
---|---|
Soldering | Good |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Poor |
Seam Weld | Poor |
Butt Weld | Poor |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Poor |
Common Fabrication Processes
Thermal Properties
Typical Uses
Applicable Specifications
Corrosion Properties