C18060
| Elements | ||||||
|---|---|---|---|---|---|---|
| Cu(1) | Sn | Co | Cr | Mg | Si | |
|
(1) Cu + Sum of Named Elements 99.9% min. |
||||||
| Min (%) | 0.01 | 0.20 | 0.01 | 0.01 | ||
| Max (%) | Rem | 0.10 | 0.15 | 0.40 | .15 | 0.15 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
Elongation (%) |
|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||
| Strip | 1/2 Hard | H02 |
58 Min 64 Typ 70 Max |
6 Min |
| Melting Point - Liquidus°F | 1978 |
|---|---|
| Melting Point - Solidus°F | 1972 |
| Densitylb/cu in. at 68°F | 0.322 |
| Specific Gravity | 8.91 |
| Electrical Conductivity% IACS at 68°F | 78 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 179 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.8 |
| Modulus of Elasticity in Tensionksi | 19300 |
| Poisson's Ratio | 0.33 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Excellent |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Excellent |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Electrical | Lead Frames, Connector Components | ||
| Relays |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.