C18095
| Elements | |||||
|---|---|---|---|---|---|
| Cu(1) | Fe | Cr | Si | Ti | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
|||||
| Min (%) | 0.15 | 0.6 | 0.01 | 0.10 | |
| Max (%) | Rem | 0.50 | 1.0 | 0.12 | 0.40 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Strip | TM06 |
91.4 Min 92.7 Typ 97.2 Max |
87.0 Min 89.8 Typ 94.3 Max |
3 Typ |
200 Typ |
|
| Melting Point - Liquidus°F | 1944 |
|---|---|
| Melting Point - Solidus°F | 1967 |
| Densitylb/cu in. at 68°F | 0.319 |
| Specific Gravity | 8.84 |
| Electrical Conductivity% IACS at 68°F | 68 |
| Modulus of Elasticity in Tensionksi | 19140 |
| Poisson's Ratioksi | 0.313 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Excellent |
| Gas Shielded Arc Welding | Excellent |
| Coated Metal Arc Welding | Excellent |
| Spot Weld | Excellent |
| Seam Weld | Excellent |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Good |
Common Fabrication Processes
No fabrication process properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Electrical | Connectors | Conductivity (Electrical) | High Strength & Conductivity |
| Lead Frames, Connector Components | Excellent Resistance to Stress Relaxation |