C18150
| Elements | |||
|---|---|---|---|
| Cu(1,2) | Cr | Zr | |
|
(1) Cu + Sum of Named Elements 99.7% min. (2) Cu value includes Ag. |
|||
| Min (%) | 0.50 | 0.02 | |
| Max (%) | Rem | 1.5 | 0.20 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Section Size (in) |
|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||
| Rod | Precipitation Heat Treated or Spinodal Heat Treated and Hard | TL04 |
81 Typ |
79 Typ |
14 Typ |
82 Typ |
0.485 |
| Precipitation Heat Treated or Spinodal Heat Treated and Hard | TL04 |
79 Typ |
75 Typ |
16 Typ |
78 Typ |
0.75 | |
| Spinodal Hardened-Low Strength (ATLS) | TX00 |
65 Min |
55 Min |
13 Min |
75 Min |
1.0 | |
| Wire | Precipitation Heat Treated or Spinodal Heat Treated and 1/2 Hard | TL02 |
68 Typ |
58 Typ |
19 Typ |
75 Typ |
0.60 |
| Precipitation Heat Treated or Spinodal Heat Treated and 1/2 Hard | TL02 |
69 Typ |
49 Typ |
15 Typ |
76 Typ |
0.70 | |
| Precipitation Heat Treated or Spinodal Heat Treated and Hard | TL04 |
68 Typ |
66 Typ |
15 Typ |
73 Typ |
0.50 | |
| Precipitation Heat Treated or Spinodal Heat Treated and Hard | TL04 |
68 Typ |
63 Typ |
20 Typ |
74 Typ |
0.60 | |
| Melting Point - Liquidus°F | 1976 |
|---|---|
| Melting Point - Solidus°F | 1958 |
| Densitylb/cu in. at 68°F | 0.321 |
| Specific Gravity | 8.89 |
| Electrical Conductivity% IACS at 68°F | 80 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 187 |
| Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 9.5 |
| Modulus of Elasticity in Tensionksi | 17000 |
Fabrication Properties
No fabrication properties for this alloy
Common Fabrication Processes
- Bending
- Cold Heading
- Machining
| Treatment | Minimum* | Maximum* | Time** | |
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
| Annealing | 1800 | 1850 | ||
| Hot Working Temperature | 1500 | 1700 | ||
| Precipitation Treatment | 800 | 3 | ||
| Solution Treatment | 0.5 | |||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Consumer | Pencil-type & Light Soldering Guns: Tips, Rod Extensions | Conductivity (Thermal) | Thermal Conductivity |
| Pencil-type & Light Soldering Guns: Tips, Rod Extensions | Mechanical Properties | Retains Strength Better Than C18200 at Elevated Temp w/ Decrease in Conduct | |
| Pencil-type & Light Soldering Guns: Tips, Rod Extensions | Mechanical Properties | Stable up to 700 F. | |
| Electrical | Resistance welding electrodes | Conductivity (Electrical) | Electrical Conductivity |
| Resistance welding electrodes | Conductivity (Thermal) | Thermal Conductivity | |
| Resistance welding electrodes | Corrosion Resistance | Oxidation Resistance | |
| Resistance welding electrodes | Mechanical Properties | High Strength | |
| Industrial | Welding Electrodes | Welding Characteristics | Weldability |
| Welding Wheels, Tips and Rod Extensions | Welding Characteristics | Weldability |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.