Find suppliers for this alloy
C18660
| Elements | |||||||
|---|---|---|---|---|---|---|---|
| Cu(1,2) | Sn | Fe | P | Cr | Mg | Si | |
|
(1) Cu + Sum of Named Elements 99.9% min. (2) Cu value includes Ag. |
|||||||
| Min (%) | 0.10 | 0.03 | 0.01 | 0.03 | 0.01 | ||
| Max (%) | Rem | 0.08 | 0.15 | 0.08 | 0.02 | 0.07 | 0.02 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||
| Flat Products | Hard | H04 |
65 Min 79 Typ 93 Max |
| Melting Point - Liquidus°F | 1960 |
|---|---|
| Melting Point - Solidus°F | 1952 |
| Densitylb/cu in. at 68°F | 0.321 |
| Specific Gravity | 8.89 |
| Electrical Conductivity% IACS at 68°F | 76 |
| Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 9.8 |
| Modulus of Elasticity in Tensionksi | 18200 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Not Recommended |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Good |
| Forgeability Rating | 650 |
| Machinability Rating | 20 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.