C19005
Elements | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | P | Ni(3) | Ag | Mg | Si | Zr | |
(1) Cu + Sum of Named Elements 99.5% min. (2) Cu value includes Ag. (3) Ni value includes Co. |
|||||||||||
Min (%) | 0.02 | 0.20 | 1.4 | 0.20 | |||||||
Max (%) | Rem | 0.05 | 0.30 | 0.7 | 0.10 | 0.05 | 1.7 | 0.50 | 0.01 | 0.35 | 0.08 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Sheet & Strip | 1/2 Hard | H02 |
58 Min 62 Typ 67 Max |
51 Min |
8 Min |
120 Min 150 Max |
Mill-hardened Temper, TM - Hard | TM04 |
75 Min 80 Typ 86 Max |
64 Min |
9 Min |
150 Min 180 Max |
|
Mill-hardened Temper, TM - XHMS Spring | TM08 |
84 Min 90 Typ 94 Max |
78 Min |
8 Min |
170 Min 200 Max |
|
Mill-hardened Temper, TM -XHM - Extra Hard | TM06 |
71 Min 75 Typ 80 Max |
59 Min |
10 Min |
170 Min |
Melting Point - Liquidus°F | 1974 |
---|---|
Melting Point - Solidus°F | 1933 |
Densitylb/cu in. at 68°F | 0.322 |
Specific Gravity | 8.81 |
Electrical Conductivity% IACS at 68°F | 60 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 142 |
Modulus of Elasticity in Tensionksi | 18900 |
Poisson's Ratio | 0.34 |
Technique | Suitability |
---|---|
Soldering | Good |
Brazing | Good |
Oxyacetylene Welding | Good |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Fair |
Spot Weld | Good |
Seam Weld | Good |
Butt Weld | Good |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Good |
Forgeability Rating | 50 |
Machinability Rating | 30 |
Common Fabrication Processes
Thermal Properties
Typical Uses
Applicable Specifications
Corrosion Properties