C19024 High Copper Alloy Wrought HIGH COPPER ALLOYS High Copper Alloys true true https://api.copper.org/alloys.xhtml/C19024
Chemical Composition
Elements
Cu(1,2) Pb Sn Zn Fe P Ni
(1) Cu + Sum of Named Elements 99.9% min.
(2) Cu value includes Ag.
Min (%) .02 0.008 0.10
Max (%) Rem 0.01 0.8 0.05 0.02 0.05 0.6
Mechanical Properties *
Form Temper Temper Code Tensile Strength
(ksi)		 YS-0.2% Offset
(ksi)		 Elongation
(%)		 Vickers Hardness, 500 gm
* Measured at room temperature, 68°F (20°C).
Flat Products 1/2 Hard H02 48 Min
58 Max
 40.5 Min
 8 Min
 90 Min
110 Max
Extra Hard H06 64 Min
72.5 Max
 58 Min
 4 Min
 120 Min
145 Max
Hard H04 55 Min
67 Max
 51.5 Min
 5 Min
 115 Min
135 Max
Spring H08 69.5 Min
 65 Min
 2 Min
 140 Min
Physical Properties
Melting Point - Liquidus°F 1976
Melting Point - Solidus°F 1958
Densitylb/cu in. at 68°F 0.322
Specific Gravity 8.9
Electrical Conductivity% IACS at 68°F 62
Modulus of Elasticity in Tensionksi 18250
Modulus of Rigidityksi 6800
Fabrication Properties
Technique Suitability
Soldering Excellent
Brazing Good
Common Fabrication Processes

No fabrication process properties for this alloy

Thermal Properties
Treatment Minimum* Maximum*
* Temperature is measured in Fahrenheit.
Solution Treatment 392 572
Annealing 932 1112
Hot Working Temperature 1292 1562