C19026
| Elements | |||||||
|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | P | Ni | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||
| Min (%) | 0.7 | 0.03 | 0.8 | 0.07 | |||
| Max (%) | Rem | 0.01 | 1.1 | 0.50 | 0.07 | 1.2 | 0.25 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Sheet & Strip | Hard | H04 |
75.4 Min 85.4 Typ 87.0 Max |
72.5 Min 78.8 Typ 85.6 Max |
8 Typ |
27 Typ |
| Melting Point - Liquidus°F | 1936 |
|---|---|
| Melting Point - Solidus°F | 1978 |
| Densitylb/cu in. at 68°F | 0.323 |
| Electrical Conductivity% IACS at 68°F | 45 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 107.7 |
| Modulus of Elasticity in Tensionksi | 18900 |
| Poisson's Ratio | 0.322 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Good |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Automotive | Connectors, automotive | ||
| Terminals | |||
| Electrical | Electrical and electronic terminals, connectors, Lead frames | ||
| Parts of the Electrical Connectors |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.