C19026
Elements | |||||||
---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | P | Ni | Si | |
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||
Min (%) | 0.7 | 0.03 | 0.8 | 0.07 | |||
Max (%) | Rem | 0.01 | 1.1 | 0.50 | 0.07 | 1.2 | 0.25 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Sheet & Strip | Hard | H04 |
75.4 Min 85.4 Typ 87.0 Max |
72.5 Min 78.8 Typ 85.6 Max |
8 Typ |
27 Typ |
Melting Point - Liquidus°F | 1936 |
---|---|
Melting Point - Solidus°F | 1978 |
Densitylb/cu in. at 68°F | 0.323 |
Electrical Conductivity% IACS at 68°F | 45 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 107.7 |
Modulus of Elasticity in Tensionksi | 18900 |
Poisson's Ratio | 0.322 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Fair |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Good |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Good |
Common Fabrication Processes
Thermal Properties
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Automotive | Connectors, automotive | ||
Terminals | |||
Electrical | Electrical and electronic terminals, connectors, Lead frames | ||
Parts of the Electrical Connectors |
Applicable Specifications
Corrosion Properties