C19160
| Elements | |||||||
|---|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | P | Ni | |
|
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. |
|||||||
| Min (%) | 0.8 | 0.15 | 0.8 | ||||
| Max (%) | Rem | 1.2 | 0.05 | 0.50 | 0.05 | 0.35 | 1.2 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Section Size (in) |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Rod | Precipitation Heat Treated or Spinodal Heat Treated and Hard | TL04 |
85 Typ |
75 Typ |
5 Typ |
0.078 |
| Wire | Precipitation Hardened | TF00 |
65 Typ |
40 Typ |
25 Typ |
0.08 |
| Precipitation Heat Treated or Spinodal Heat Treated and 1/2 Hard | TL02 |
86 Typ |
70 Typ |
7 Typ |
0.08 | |
| Precipitation Heat Treated or Spinodal Heat Treated and 1/4 Hard | TL01 |
78.5 Typ |
68 Typ |
12 Typ |
0.08 | |
| Precipitation Heat Treated or Spinodal Heat Treated and Hard | TL04 |
95 Typ |
75 Typ |
5 Typ |
0.08 | |
| Precipitation Heat Treated or Spinodal Heat Treated and Spring | TL08 |
107 Typ |
98 Typ |
3 Typ |
0.08 | |
| (1)Volume basis, after aging treatment (2)After aging treatment | |
| Melting Point - Liquidus°F | 1980 |
|---|---|
| Melting Point - Solidus°F | 1900 |
| Densitylb/cu in. at 68°F | 0.32 |
| Specific Gravity | 8.88 |
| Electrical Conductivity% IACS at 68°F | 55 (1) |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 146 (2) |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.8 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.092 |
| Modulus of Elasticity in Tensionksi | 18000 |
| Modulus of Rigidityksi | 6000 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Poor |
| Machinability Rating | 80 |
Common Fabrication Processes
- Cold Heading
- Machining
| Treatment | Minimum* | Maximum* | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. | ||||
| Hot Working Temperature | 1400 | 1600 | ||
| Precipitation Treatment | 800 | |||
| Solution Treatment | 1300 | 1450 | ||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Electrical | Connector Pins | ||
| Contacts | Conductivity (Electrical) | Electrical Conductivity | |
| Contacts | Conductivity (Thermal) | Thermal Conductivity | |
| Contacts | Corrosion Resistance | Corrosion Resistance | |
| Contacts | Mechanical Properties | Moderate Strength | |
| Contacts | Solderability | Solderability | |
| Sockets | Conductivity (Electrical) | Electrical Conductivity | |
| Sockets | Conductivity (Thermal) | Thermal Conductivity | |
| Sockets | Corrosion Resistance | Corrosion Resistance | |
| Sockets | Mechanical Properties | High Strength |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.