C19217
| Elements | ||||
|---|---|---|---|---|
| Cu(1) | Fe | P | Mn | |
|
(1) Cu + Sum of Named Elements, 99.95% min. |
||||
| Min (%) | 0.09 | 0.05 | 0.05 | |
| Max (%) | Rem | 0.20 | 0.09 | 0.20 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Strip | Hard | H04 |
58 Min 65 Typ 72 Max |
54 Min 61 Typ 68 Max |
4 Min |
120 Min 145 Max |
| Melting Point - Liquidus°F | 1976 |
|---|---|
| Melting Point - Solidus°F | 1931 |
| Densitylb/cu in. at 68°F | 0.322 |
| Specific Gravity | 8.93 |
| Electrical Conductivity% IACS at 68°F | 80 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 192 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.5 |
| Modulus of Elasticity in Tensionksi | 18000 |
| Poisson's Ratio | 0.33 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Excellent |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Excellent |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.