C19217
Elements | ||||
---|---|---|---|---|
Cu(1) | Fe | P | Mn | |
(1) Cu + Sum of Named Elements, 99.95% min. |
||||
Min (%) | 0.09 | 0.05 | 0.05 | |
Max (%) | Rem | 0.20 | 0.09 | 0.20 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Strip | Hard | H04 |
58 Min 65 Typ 72 Max |
54 Min 61 Typ 68 Max |
4 Min |
120 Min 145 Max |
Melting Point - Liquidus°F | 1976 |
---|---|
Melting Point - Solidus°F | 1931 |
Densitylb/cu in. at 68°F | 0.322 |
Specific Gravity | 8.93 |
Electrical Conductivity% IACS at 68°F | 80 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 192 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.5 |
Modulus of Elasticity in Tensionksi | 18000 |
Poisson's Ratio | 0.33 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Good |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Excellent |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Good |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Excellent |