Find suppliers for this alloy
C19250
| Elements | ||||||||
|---|---|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | P | Mn | Si | |
|
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.8% min. |
||||||||
| Min (%) | 95.8 | 0.8 | 0.15 | 0.04 | ||||
| Max (%) | 0.02 | 2.5 | 1.0 | 0.45 | 0.20 | 0.02 | 0.010 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||
| Flat Products | 1/2 Hard | H02 |
58 Min 73 Typ 80 Max |
54 Min 70 Typ 77 Max |
6 Typ |
| Extra Spring | H10 |
106 Min 109 Typ 119 Max |
99 Min 106 Typ 117 Max |
||
| Hard | H04 |
73 Min 87 Typ 94 Max |
70 Min 84 Typ 91 Max |
5 Typ |
|
| Spring | H08 |
80 Min 94 Typ 109 Max |
777 Min 91 Typ 106 Max |
5 Typ |
|
| Melting Point - Liquidus°F | 1954 |
|---|---|
| Densitylb/cu in. at 68°F | 0.321 |
| Electrical Conductivity% IACS at 68°F | 30 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 75 |
| Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 9.7 |
| Modulus of Elasticity in Tensionksi | 17400 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Excellent |
| Seam Weld | Excellent |
| Butt Weld | Excellent |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Fair |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.