Find suppliers for this alloy
C19419
Elements | |||||||||
---|---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | P | Ni(3) | Mn | Si | |
(1) Cu + Sum of Named Elements 99.8% min. (2) Cu value includes Ag. (3) Ni value includes Co. |
|||||||||
Min (%) | 96.7 | 0.05 | 0.10 | 1.7 | 0.03 | ||||
Max (%) | 0.02 | 0.18 | 0.40 | 2.3 | 0.03 | 0.04 | 0.04 | 0.09 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||
Flat Products | 1/2 Hard | H02 |
61 Min 65 Typ 70 Max |
55 Min 61 Typ 67 Max |
14 Typ |
1/4 Hard | H01 |
54 Min 58 Typ 62 Max |
41 Min 46 Typ 52 Max |
20 Typ |
|
Hard | H04 |
71 Min 78 Typ 81 Max |
64 Min 70 Typ 75 Max |
5 Typ |
Melting Point - Liquidus°F | 1962 |
---|---|
Melting Point - Solidus°F | 1920 |
Densitylb/cu in. at 68°F | 0.321 |
Electrical Conductivity% IACS at 68°F | 50 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 172 |
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 9.94 |
Modulus of Elasticity in Tensionksi | 17400 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Good |
Seam Weld | Good |
Butt Weld | Good |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Fair |
Common Fabrication Processes
Thermal Properties
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Automotive | Electrical terminals | ||
Electrical | Electrical and electronic terminals,connectors, busbars |
Applicable Specifications
Corrosion Properties