C19800
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1) | Sn | Zn | Fe | P | Mg | |
(1) Cu + Sum of Named Elements 99.8% min. |
||||||
Min (%) | 0.10 | 0.30 | 0.02 | 0.01 | 0.10 | |
Max (%) | Rem | 1.0 | 1.5 | 0.50 | 0.10 | 1.0 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm | Fatigue Strength** (ksi) |
Proportional Limit (ksi) |
Section Size (in) |
---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||
Flat Products | 1/2 Hard | H02 |
63 Typ |
61 Typ |
12 Typ |
131 Typ |
55 Typ | ||
Extra Hard | H06 |
80 Typ |
80 Typ |
9 Typ |
166 Typ |
65 Typ | |||
Hard | H04 |
72 Typ |
69 Typ |
10 Typ |
149 Typ |
36 Typ | 57 Typ | 0.012 |
Melting Point - Liquidus°F | 1963 |
---|---|
Melting Point - Solidus°F | 1920 |
Densitylb/cu in. at 68°F | 0.322 |
Specific Gravity | 8.9 |
Electrical Conductivity% IACS at 68°F | 61 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 150 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10.2 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.094 |
Modulus of Elasticity in Tensionksi | 11800 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Gas Shielded Arc Welding | Good |
Spot Weld | Good |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Good |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | Value* | |
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Stress Relief | 482 | |||
Annealing | 482 | |||
Hot Working Temperature | 1472 | 1832 |
Typical Uses
Applicable Specifications
Corrosion Properties