C19920
| Elements | |||||
|---|---|---|---|---|---|
| Cu(1) | Pb | Al | Ti | Nb | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
|||||
| Min (%) | 0.01 | 2.5 | 0.01 | ||
| Max (%) | Rem | 0.05 | 0.30 | 3.5 | 0.30 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Strip | Precipitation or Spinodal Heat-treated, Spring and Thermal Stress Relieved | TR08 |
143.5 Min 161 Typ 168.2 Max |
137.8 Min 142.1 Typ 152.3 Max |
1 Typ |
329 Typ |
| Densitylb/cu in. at 68°F | 0.313 |
|---|---|
| Specific Gravity | 8.66 |
| Electrical Conductivity% IACS at 68°F | 13 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 19 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.87 |
| Modulus of Elasticity in Tensionksi | 18565 |
| Poisson's Ratioksi | 0.347 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Excellent |
| Gas Shielded Arc Welding | Excellent |
| Coated Metal Arc Welding | Excellent |
| Spot Weld | Excellent |
| Seam Weld | Excellent |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Good |
| Forgeability Rating | 99 |
| Machinability Rating | 60 |
Common Fabrication Processes
No fabrication process properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Electrical | Electrical Connectors | Excellent Resistance to Stress Relaxation | |
| Terminals | Super High Strength |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.