C27250
| Elements | ||||||||
|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Zn | Fe | P | Bi | C | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
||||||||
| Min (%) | 62.0 | 0.05 | 0.20 | |||||
| Max (%) | 65.0 | 0.009 | Rem | 0.35 | 0.40 | 0.009 | 1.2 | 0.009 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Impact Strength (ft-lbs) |
|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||
| Rod, Bar & Forging | 1/2 Hard | H02 |
45 Min 49 Typ |
25 Min 30 Typ |
13 Min 26 Typ |
56 Typ |
12 Typ |
| Densitylb/cu in. at 68°F | 0.295 |
|---|---|
| Specific Gravity | 8.17 |
| Electrical Conductivity% IACS at 68°F | 21 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 12 |
| Modulus of Elasticity in Tensionksi | 6700 |
| Modulus of Rigidityksi | 5750 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Good |
| Seam Weld | Not Recommended |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Fair |
| Forgeability Rating | 80 |
| Machinability Rating | 90 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.