C27453
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | As | |
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
Min (%) | 61.5 | 0.02 | ||||
Max (%) | 63.5 | 0.25 | 0.15 | Rem | 0.15 | 0.15 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Rod & Shapes | Cold-worked Tempers, H | H |
49 Min 52 Typ 58 Max |
29 Min 35 Typ |
30 Typ |
110 Typ |
Melting Point - Liquidus°F | 1680 |
---|---|
Melting Point - Solidus°F | 1650 |
Densitylb/cu in. at 68°F | 0.31 |
Specific Gravity | 8.42 |
Electrical Conductivity% IACS at 68°F | 28 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 68 |
Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 11 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 12 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 15000 |
Modulus of Rigidityksi | 5600 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Good |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Excellent |
Seam Weld | Not Recommended |
Butt Weld | Good |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Excellent |
Forgeability Rating | 90 |
Machinability Rating | 40 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Solution Treatment | 480 | 660 | ||
Annealing | 840 | 1200 | ||
Hot Working Temperature | 1200 | 1470 |
Typical Uses
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Forgings, Die (Hot Pressed) | ASME | SB283 | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | ||
Hot-Pressed | ASTM | B283/B283M | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) |
Corrosion Properties