C27460
| Elements | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Al | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||||
| Min (%) | 60.0 | 0.15 | 0.15 | 0.20 | 0.080 | 0.060 | |||
| Max (%) | 62.0 | 0.25 | 0.35 | Rem | 0.10 | 0.25 | 0.35 | 0.16 | 0.090 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Rockwell B scale |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Rod & Bar | 1/2 Hard | H02 |
67 Typ |
47 Typ |
25 Typ |
68 Typ |
| Melting Point - Liquidus°F | 1680 |
|---|---|
| Melting Point - Solidus°F | 1650 |
| Densitylb/cu in. at 68°F | 0.31 |
| Specific Gravity | 8.44 |
| Electrical Conductivity% IACS at 68°F | 20 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 65 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.4 |
| Modulus of Elasticity in Tensionksi | 15000 |
| Modulus of Rigidityksi | 5500 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Good |
| Seam Weld | Not Recommended |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 95 |
| Machinability Rating | 70 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Plumbing | Fixtures | ||
| Low Lead Valves and Fittings | |||
| Plumbers Fittings |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.