Find suppliers for this alloy
C31600
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1) | Pb | Zn | Fe | P | Ni | |
(1) Cu + Sum of Named Elements 99.6% min. |
||||||
Min (%) | 87.5 | 1.3 | 0.04 | 0.7 | ||
Max (%) | 90.5 | 2.5 | Rem | 0.10 | 0.10 | 1.2 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Shear Strength (ksi) |
Section Size (in) |
Cold Work (%) |
---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||||||
Bar | Hard | H04 |
63 Typ |
56 Typ |
12 Typ |
70 Typ |
0.25 | ||
Rod | Hard | H04 |
67 Typ |
59 Typ |
13 Typ |
72 Typ |
40 Typ |
0.5 | 38 |
Hard | H04 |
65 Typ |
57 Typ |
15 Typ |
70 Typ |
39 Typ |
1 | 38 | |
Nominal Grain Size 0.050 mm | OS050 |
37 Typ |
12 Typ |
45 Typ |
24 Typ |
1 |
Melting Point - Liquidus°F | 1900 |
---|---|
Melting Point - Solidus°F | 1850 |
Densitylb/cu in. at 68°F | 0.32 |
Specific Gravity | 8.86 |
Electrical Conductivity% IACS at 68°F | 32 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 81 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10.2 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 17000 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Fair |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Poor |
Machinability Rating | 80 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 800 | 1200 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Builders Hardware | Hardware | Appearance | Appearance |
Hardware | Corrosion Resistance | Corrosion Resistance | |
Hardware | Forming Characteristics | Formability | |
Hardware | Machining Characteristics | Machinability | |
Electrical | Connectors | Conductivity (Electrical) | Electrical Conductivity |
Connectors | Conductivity (Thermal) | Thermal Conductivity | |
Connectors | Corrosion Resistance | Corrosion Resistance | |
Connectors | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Connectors | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Fasteners | Fasteners | Appearance | Appearance |
Fasteners | Conductivity (Electrical) | Electrical Conductivity | |
Fasteners | Conductivity (Thermal) | Thermal Conductivity | |
Fasteners | Corrosion Resistance | Corrosion Resistance | |
Fasteners | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Fasteners | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Fasteners | Forming Characteristics | Formability | |
Fasteners | Machining Characteristics | Machinability | |
Nuts | Appearance | Appearance | |
Nuts | Corrosion Resistance | Corrosion Resistance | |
Nuts | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Nuts | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Nuts | Forming Characteristics | Formability | |
Nuts | Machining Characteristics | Machinability | |
Screws | Appearance | Appearance | |
Screws | Corrosion Resistance | Corrosion Resistance | |
Screws | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Screws | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Screws | Machining Characteristics | Machinability | |
Industrial | Screw Machine Parts | Corrosion Resistance | Corrosion Resistance |
Screw Machine Parts | Machining Characteristics | Machinability |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Bar | ASTM | B140/B140M | COPPER-ZINC-LEAD (LEADED RED BRASS HARDWARE BRONZE) ROD, BAR AND SHAPES | ||
Rod | ASTM | B140/B140M | COPPER-ZINC-LEAD (LEADED RED BRASS HARDWARE BRONZE) ROD, BAR AND SHAPES | ||
Shapes | ASTM | B140/B140M | COPPER-ZINC-LEAD (LEADED RED BRASS HARDWARE BRONZE) ROD, BAR AND SHAPES | ||
Valves | MILITARY | MIL-V-18436 | VALVES, CHECK, BRONZE |
Corrosion Properties