C35350
Elements | |||||||
---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni | |
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||
Min (%) | 61.0 | 2.0 | 0.05 | ||||
Max (%) | 63.0 | 4.5 | 0.6 | Rem | 0.4 | 0.2 | 0.3 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm | Impact Strength (ft-lbs) |
Fatigue Strength** (ksi) |
---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | ||||||||
Rod | 1/2 Hard | H02 |
50 Min 64 Typ 69 Max |
39 Min 60 Typ 64 Max |
25 Typ |
140 Typ |
21 Typ | 25 Typ |
Melting Point - Liquidus°F | 1654 |
---|---|
Melting Point - Solidus°F | 1578 |
Densitylb/cu in. at 68°F | 0.301 |
Specific Gravity | 8.4 |
Electrical Conductivity% IACS at 68°F | 23 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 61.3 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 12.2 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 17600 |
Modulus of Rigidityksi | 4560 |
Poisson's Ratio | 0.26 |
Technique | Suitability |
---|---|
Soldering | Good |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Not Recommended |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Poor |
Machinability Rating | 88 |
Common Fabrication Processes
Thermal Properties
Typical Uses
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Rod, Bar & Shapes | ASTM | B453/B453M | COPPER-ZINC-LEAD ALLOY (LEADED-BRASS) ROD |
Corrosion Properties