Find suppliers for this alloy C35350
Chemical Composition
Elements
Cu(1) Pb Sn Zn Fe P Ni
(1) Cu + Sum of Named Elements 99.5% min.
Min (%) 61.0 2.0 0.05
Max (%) 63.0 4.5 0.6 Rem 0.4 0.2 0.3
Mechanical Properties *
Form Temper Temper Code Tensile Strength
(ksi)
YS-0.2% Offset
(ksi)
Elongation
(%)
Vickers Hardness, 500 gm Impact Strength
(ft-lbs)
Fatigue Strength**
(ksi)
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106.
Rod 1/2 Hard H02 50 Min
64 Typ
69 Max
39 Min
60 Typ
64 Max
25 Typ
140 Typ
21 Typ 25 Typ
Physical Properties
Melting Point - Liquidus°F 1654
Melting Point - Solidus°F 1578
Densitylb/cu in. at 68°F 0.301
Specific Gravity 8.4
Electrical Conductivity% IACS at 68°F 23
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F 61.3
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) 12.2
Specific Heat CapacityBtu/ lb /°F at 68°F 0.09
Modulus of Elasticity in Tensionksi 17600
Modulus of Rigidityksi 4560
Poisson's Ratio 0.26
Fabrication Properties
Technique Suitability
Soldering Good
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Coated Metal Arc Welding Not Recommended
Spot Weld Not Recommended
Seam Weld Not Recommended
Butt Weld Not Recommended
Capacity for Being Cold Worked Poor
Capacity for Being Hot Formed Poor
Machinability Rating 88
Common Fabrication Processes

No fabrication process properties for this alloy

Thermal Properties

No thermal properties for this alloy

Typical Uses

No information for this alloy

Applicable Specifications
Form Specific Sub-Form Application System Standard Description
Rod, Bar & Shapes ASTM B453/B453M COPPER-ZINC-LEAD ALLOY (LEADED-BRASS) ROD
Corrosion Properties

No Corrosion Properties Available.