C36200
| Elements | ||||
|---|---|---|---|---|
| Cu | Pb | Zn | Fe | |
| Min (%) | 60.0 | 3.5 | ||
| Max (%) | 63.0 | 4.5 | Rem | 0.15 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Rockwell F scale | Shear Strength (ksi) |
Fatigue Strength** (ksi) |
Section Size (in) |
Cold Work (%) |
|---|---|---|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||||
| Flat Products | 1/4 Hard | H01 |
56 Typ |
45 Typ |
20 Typ |
62 Typ |
33 Typ |
0.25 | 11 | ||
| Rod | 1/2 Hard | H02 |
68 Typ |
52 Typ |
18 Typ |
80 Typ |
38 Typ |
0.25 | 25 | ||
| 1/2 Hard | H02 |
55 Typ |
44 Typ |
32 Typ |
75 Typ |
32 Typ |
20 Typ | 2 | 15 | ||
| 1/2 Hard | H02 |
58 Typ |
45 Typ |
25 Typ |
78 Typ |
34 Typ |
1 | 20 | |||
| Soft Anneal | O60 |
49 Typ |
18 Typ |
53 Typ |
68 Typ |
30 Typ |
1 | ||||
| Shapes | 1/4 Hard | H01 |
56 Typ |
45 Typ |
20 Typ |
62 Typ |
33 Typ |
0.5 | 11 | ||
| As Hot Extruded | M30 |
56 Typ |
45 Typ |
20 Typ |
62 Typ |
33 Typ |
0.5 | ||||
| Melting Point - Liquidus°F | 1650 |
|---|---|
| Melting Point - Solidus°F | 1630 |
| Densitylb/cu in. at 68°F | 0.307 |
| Specific Gravity | 8.5 |
| Electrical Conductivity% IACS at 68°F | 26 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 67 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.4 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 14000 |
| Modulus of Rigidityksi | 5300 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Fair |
| Machinability Rating | 100 |
Common Fabrication Processes
- Machining
- Roll Threading and Knurling
| Treatment | Minimum* | Maximum* | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. | ||||
| Annealing | 800 | 1100 | ||
| Hot Working Temperature | 1300 | 1450 | ||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Industrial | Automatic Screw Machine Parts | Corrosion Resistance | Corrosion Resistance |
| Automatic Screw Machine Parts | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Automatic Screw Machine Parts | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Automatic Screw Machine Parts | Machining Characteristics | Machinability | |
| Automatic Screw Machine Parts | Mechanical Properties | Moderate Strength | |
| Gears | Corrosion Resistance | Corrosion Resistance | |
| Gears | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Gears | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Gears | Friction & Wear Properties | Wear Resistance | |
| Gears | Machining Characteristics | Machinability | |
| Gears | Mechanical Properties | Moderate Strength | |
| Pinions | Corrosion Resistance | Corrosion Resistance | |
| Pinions | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Pinions | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Pinions | Friction & Wear Properties | Wear Resistance | |
| Pinions | Machining Characteristics | Machinability | |
| Pinions | Mechanical Properties | Moderate Strength |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.