C36200
Elements | ||||
---|---|---|---|---|
Cu | Pb | Zn | Fe | |
Min (%) | 60.0 | 3.5 | ||
Max (%) | 63.0 | 4.5 | Rem | 0.15 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Rockwell F scale | Shear Strength (ksi) |
Fatigue Strength** (ksi) |
Section Size (in) |
Cold Work (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||||
Flat Products | 1/4 Hard | H01 |
56 Typ |
45 Typ |
20 Typ |
62 Typ |
33 Typ |
0.25 | 11 | ||
Rod | 1/2 Hard | H02 |
68 Typ |
52 Typ |
18 Typ |
80 Typ |
38 Typ |
0.25 | 25 | ||
1/2 Hard | H02 |
55 Typ |
44 Typ |
32 Typ |
75 Typ |
32 Typ |
20 Typ | 2 | 15 | ||
1/2 Hard | H02 |
58 Typ |
45 Typ |
25 Typ |
78 Typ |
34 Typ |
1 | 20 | |||
Soft Anneal | O60 |
49 Typ |
18 Typ |
53 Typ |
68 Typ |
30 Typ |
1 | ||||
Shapes | 1/4 Hard | H01 |
56 Typ |
45 Typ |
20 Typ |
62 Typ |
33 Typ |
0.5 | 11 | ||
As Hot Extruded | M30 |
56 Typ |
45 Typ |
20 Typ |
62 Typ |
33 Typ |
0.5 |
Melting Point - Liquidus°F | 1650 |
---|---|
Melting Point - Solidus°F | 1630 |
Densitylb/cu in. at 68°F | 0.307 |
Specific Gravity | 8.5 |
Electrical Conductivity% IACS at 68°F | 26 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 67 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.4 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 14000 |
Modulus of Rigidityksi | 5300 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Fair |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Fair |
Machinability Rating | 100 |
Common Fabrication Processes
- Machining
- Roll Threading and Knurling
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 800 | 1100 | ||
Hot Working Temperature | 1300 | 1450 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Industrial | Automatic Screw Machine Parts | Corrosion Resistance | Corrosion Resistance |
Automatic Screw Machine Parts | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Automatic Screw Machine Parts | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Automatic Screw Machine Parts | Machining Characteristics | Machinability | |
Automatic Screw Machine Parts | Mechanical Properties | Moderate Strength | |
Gears | Corrosion Resistance | Corrosion Resistance | |
Gears | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Gears | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Gears | Friction & Wear Properties | Wear Resistance | |
Gears | Machining Characteristics | Machinability | |
Gears | Mechanical Properties | Moderate Strength | |
Pinions | Corrosion Resistance | Corrosion Resistance | |
Pinions | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
Pinions | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Pinions | Friction & Wear Properties | Wear Resistance | |
Pinions | Machining Characteristics | Machinability | |
Pinions | Mechanical Properties | Moderate Strength |
Applicable Specifications
Corrosion Properties