C41120
Elements | |||||||
---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni | |
(1) Cu + Sum of Named Elements 99.7% min. |
|||||||
Min (%) | 89.0 | 0.30 | 0.05 | 0.01 | 0.05 | ||
Max (%) | 92.0 | 0.05 | 0.7 | Rem | 0.20 | 0.35 | 0.20 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||
Flat Products | 1/2 Hard | H02 |
67 Typ |
60 Typ |
12 Typ |
1/4 Hard | H01 |
60 Typ |
40 Typ |
24 Typ |
|
Extra Hard | H06 |
84 Typ |
81 Typ |
5 Typ |
|
Hard | H04 |
78 Typ |
73 Typ |
8 Typ |
|
Nominal Grain Size 0.015 mm | OS015 |
54 Typ |
30 Typ |
40 Typ |
|
Spring | H08 |
89 Typ |
85 Typ |
4 Typ |
Melting Point - Liquidus°F | 1905 |
---|---|
Melting Point - Solidus°F | 1870 |
Densitylb/cu in. at 68°F | 0.318 |
Specific Gravity | 8.8 |
Electrical Conductivity% IACS at 68°F | 40 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 100 |
Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 10.2 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 17000 |
Modulus of Rigidityksi | 6700 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Fair |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Fair |
Seam Weld | Not Recommended |
Butt Weld | Good |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Good |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 660 | 1350 |
Typical Uses
Applicable Specifications
Corrosion Properties