Find suppliers for this alloy
C42230
| Elements | ||||||||
|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | Co | Mn | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
||||||||
| Min (%) | 87.0 | 0.40 | 0.30 | 0.05 | ||||
| Max (%) | 91.0 | 0.01 | 1.5 | Rem | 0.05 | 1.5 | 0.05 | 0.30 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||
| Strip | Hard | H04 |
84.1 Min 93.7 Typ 92.3 Max |
79.8 Min 82.2 Typ 92.8 Max |
197 Typ |
| Melting Point - Liquidus°F | 1940 |
|---|---|
| Melting Point - Solidus°F | 1839 |
| Densitylb/cu in. at 68°F | 0.316 |
| Specific Gravity | 8.75 |
| Electrical Conductivity% IACS at 68°F | 34 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 73.2 |
| Modulus of Elasticity in Tensionksi | 17300 |
| Poisson's Ratio | 0.345 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Good |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Electrical | Conductors | ||
| Terminals Connectors |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.