Find suppliers for this alloy
C42300
| Elements | ||||||
|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Ni | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
| Min (%) | 87.0 | 0.50 | 0.50 | 0.10 | ||
| Max (%) | 91.0 | 0.01 | 1.5 | Rem | 1.5 | 0.30 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Sheet & Strip | Hard | H04 |
84.1 Min 90.1 Typ |
79.8 Min 85.9 Typ 92.8 Max |
4 Typ |
187 Typ |
| Melting Point - Liquidus°F | 1854 |
|---|---|
| Melting Point - Solidus°F | 1868 |
| Densitylb/cu in. at 68°F | 0.323 |
| Specific Gravity | 8.94 |
| Electrical Conductivity% IACS at 68°F | 32 |
| Modulus of Elasticity in Tensionksi | 17400 |
| Poisson's Ratio | 0.308 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Not Recommended |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Good |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Electrical | Electrical terminals | ||
| Relay Elements | |||
| Terminals Connectors |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.