C42300
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Ni | Si | |
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
Min (%) | 87.0 | 0.50 | 0.50 | 0.10 | ||
Max (%) | 91.0 | 0.01 | 1.5 | Rem | 1.5 | 0.30 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Sheet & Strip | Hard | H04 |
84.1 Min 90.1 Typ |
79.8 Min 85.9 Typ 92.8 Max |
4 Typ |
187 Typ |
Melting Point - Liquidus°F | 1854 |
---|---|
Melting Point - Solidus°F | 1868 |
Densitylb/cu in. at 68°F | 0.323 |
Specific Gravity | 8.94 |
Electrical Conductivity% IACS at 68°F | 32 |
Modulus of Elasticity in Tensionksi | 17400 |
Poisson's Ratio | 0.308 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Not Recommended |
Oxyacetylene Welding | Fair |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Good |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Good |
Common Fabrication Processes
Thermal Properties
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Electrical | Electrical terminals | ||
Relay Elements | |||
Terminals Connectors |
Applicable Specifications
Corrosion Properties