C46270
| Elements | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Mn | Si | |
|
(1) Cu + Sum of Named Elements, 99.95% min. |
|||||||||
| Min (%) | 62.0 | 0.8 | 0.6 | ||||||
| Max (%) | 65.0 | 0.10 | 1.5 | Rem | 0.10 | 0.20 | 0.10 | 0.10 | 1.2 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Rod | 1/2 Hard | H02 |
82.7 Typ |
50.8 Typ |
4 Min |
175 Typ |
| As Hot Extruded | M30 |
72.5 Typ |
50.8 Typ |
10 Min |
150 Typ |
|
| Melting Point - Liquidus°F | 1598 |
|---|---|
| Melting Point - Solidus°F | 1580 |
| Densitylb/cu in. at 68°F | 0.301 |
| Specific Gravity | 8.33 |
| Electrical Conductivity% IACS at 68°F | 14 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Not Recommended |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 95 |
| Machinability Rating | 80 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Fasteners | Screw Machine Products | ||
| Plumbing | Fittings and valves | ||
| Plumbers Fittings | |||
| Valve Bodies, Faucets, Plumbing Components |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.