C48640
| Elements | |||||||
|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | Ni | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||
| Min (%) | 59.0 | 1.0 | 0.50 | 0.05 | |||
| Max (%) | 62.0 | 3.0 | 2.0 | Rem | 0.40 | 0.25 | 0.3 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Strip, Rod, Bar, Wire & Forgings | 1/2 Hard | H02 |
59 Typ |
35 Typ |
35 Min |
110 Min |
| As Hot Extruded | M30 |
58 Typ |
27 Typ |
36 Min |
105 Min |
|
| Melting Point - Liquidus°F | 1639 |
|---|---|
| Melting Point - Solidus°F | 1591 |
| Densitylb/cu in. at 68°F | 0.303 |
| Specific Gravity | 8.4 |
| Electrical Conductivity% IACS at 68°F | 22.4 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 59.3 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.9 |
| Modulus of Elasticity in Tensionksi | 16000 |
| Modulus of Rigidityksi | 6000 |
| Poisson's Ratio | 0.33 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Not Recommended |
| Capacity for Being Cold Worked | Fair |
| Capacity for Being Hot Formed | Good |
| Forgeability Rating | 95 |
| Machinability Rating | 92 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Plumbing | Fittings and valves | ||
| Plumbing Fittiings |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.