C48640
Elements | |||||||
---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni | |
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||
Min (%) | 59.0 | 1.0 | 0.50 | 0.05 | |||
Max (%) | 62.0 | 3.0 | 2.0 | Rem | 0.40 | 0.25 | 0.3 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
Strip, Rod, Bar, Wire & Forgings | 1/2 Hard | H02 |
59 Typ |
35 Typ |
35 Min |
110 Min |
As Hot Extruded | M30 |
58 Typ |
27 Typ |
36 Min |
105 Min |
Melting Point - Liquidus°F | 1639 |
---|---|
Melting Point - Solidus°F | 1591 |
Densitylb/cu in. at 68°F | 0.303 |
Specific Gravity | 8.4 |
Electrical Conductivity% IACS at 68°F | 22.4 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 59.3 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.9 |
Modulus of Elasticity in Tensionksi | 16000 |
Modulus of Rigidityksi | 6000 |
Poisson's Ratio | 0.33 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Good |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Not Recommended |
Capacity for Being Cold Worked | Fair |
Capacity for Being Hot Formed | Good |
Forgeability Rating | 95 |
Machinability Rating | 92 |
Common Fabrication Processes
Thermal Properties
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Plumbing | Fittings and valves | ||
Plumbing Fittiings |
Applicable Specifications
Corrosion Properties