C49100
| Elements | ||||||||
|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | Ni | Te | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
||||||||
| Min (%) | 85.5 | .30 | ||||||
| Max (%) | 87.5 | .09 | .30 | 14.5 | .30 | .10 | .30 | .9 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Rod, Bar & Wire | 1/2 Hard | H02 |
50 Min |
31 Min |
16 Typ |
58 Min 75 Max |
| Melting Point - Liquidus°F | 1880 |
|---|---|
| Melting Point - Solidus°F | 1810 |
| Densitylb/cu in. at 68°F | 0.316 |
| Specific Gravity | 8.75 |
| Electrical Conductivity% IACS at 68°F | 37 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 92 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10.4 |
| Modulus of Elasticity in Tensionksi | 17000 |
| Modulus of Rigidityksi | 6400 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Fair |
| Seam Weld | Not Recommended |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Good |
| Forgeability Rating | 75 |
| Machinability Rating | 92 |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Plumbing | Lead-free, dezinfication resistant alloy for potable water components | ||
| Plumbing & Pipe Fittings | |||
| Plumbing Castings | |||
| Potable water valve bodies, faucets, plumbing components |
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.