C49260
| Elements | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | Bi | Cd | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||||
| Min (%) | 58.0 | 0.05 | 0.50 | ||||||
| Max (%) | 63.0 | 0.09 | 0.50 | Rem | 0.50 | 0.15 | 1.8 | 0.001 | 0.10 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm | Ultimate Tensile Strength in Shear (ksi) |
Section Size (in) |
|---|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | |||||||||
| Die Forging | As Hot Forged - Air Cooled | M10 | 22 Min |
25 Min |
52 Min |
||||
| Rod, Bar & Wire | 1/2 Hard | H02 |
55 Min |
25 Min |
15 Min |
80 Typ |
0.3 - 1.0 | ||
| Annealed | O61 |
50 Min |
20 Min |
15 Min |
80 Typ |
0.3 - 1.0 | |||
| As Hot Extruded | M30 |
50 Min |
20 Min |
10 Min |
1.0 - 4.37 | ||||
| Extruded and Drawn | H50 |
50 Min |
20 Min |
||||||
| Hard | H04 |
67 Min |
45 Min |
3 Min |
0.08 - 0.3 | ||||
| Melting Point - Liquidus°F | 1670 |
|---|---|
| Melting Point - Solidus°F | 1623 |
| Densitylb/cu in. at 68°F | 0.301 |
| Specific Gravity | 8.4 |
| Electrical Conductivity% IACS at 68°F | 21.7 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 45.5 |
| Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 7.33 |
| Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 9 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10.1 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 15800 |
| Modulus of Rigidityksi | 5600 |
| Magnetic Permeability | 1.58 |
| Technique | Suitability |
|---|---|
| Soldering | Good |
| Brazing | Good |
| Capacity for Being Cold Worked | Fair |
| Capacity for Being Hot Formed | Fair |
| Forgeability Rating | 70 |
| Machinability Rating | 90 |
Common Fabrication Processes
No fabrication process properties for this alloy
| Treatment | Minimum* | |||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. | ||||
| Annealing | 932 | |||
| Hot Working Temperature | 1328 | |||
| Stress Relief | 572 | |||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Automotive | Electric & Electronic parts | ||
| Plumbing | Enviornmentaly friendly Faucets and Plumbing Components |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| Forgings, Die (Hot Pressed) | ASTM | B283/B283M | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | ||
| ASME | SB283 | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | |||
| Rod, Bar & Shapes | Forgings | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES | |
| Rod, Bar & Wire | Free-Cutting | ASTM | B974/B974M | FREE-CUTTING BISMUTH BRASS ROD, BAR AND WIRE | |
| ASTM | B967/B967M | COPPER-ZINC-TIN-BISMUTH ALLOY ROD, BAR AND WIRE |