C49300
Elements | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | Ni | Bi | Cd | Sb | Si | Se | |
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||||||
Min (%) | 58.0 | 1.0 | 0.5 | ||||||||
Max (%) | 62.0 | 0.09 | 1.8 | Rem | 0.10 | 0.3 | 2.5 | 0.0075 | 0.50 | 0.10 | 0.20 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm | Shear Strength (ksi) |
Compressive Yield Strength (ksi) |
Fatigue Strength** (ksi) |
Section Size (in) |
---|---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | ||||||||||
Bar | 1/2 Hard | H02 |
67 Typ |
59 Typ |
9 Typ |
159 Typ |
1 | |||
Annealed | O61 |
64 Typ |
41 Typ |
18 Typ |
133 Typ |
1 | ||||
As Hot Extruded | M30 |
62 Typ |
31 Typ |
20 Typ |
1 | |||||
Hard | H04 | 60 Typ |
5 Typ |
190 Typ |
42 Typ |
261 Typ | 29 Typ | 0.2 | ||
Rod | 1/2 Hard | H02 |
67 Typ |
59 Typ |
9 Typ |
159 Typ |
1 | |||
Annealed | O61 |
64 Typ |
41 Typ |
18 Typ |
133 Typ |
1 | ||||
As Hot Extruded | M30 |
62 Typ |
31 Typ |
20 Typ |
1 | |||||
Hard | H04 |
75 Typ |
60 Typ |
5 Typ |
.02 | |||||
Wire | Hard | H04 |
67 Min |
45 Min |
3 Min |
.08 |
Melting Point - Liquidus°F | 1616 |
---|---|
Melting Point - Solidus°F | 1544 |
Densitylb/cu in. at 68°F | 0.3 |
Specific Gravity | 8.44 |
Electrical Conductivity% IACS at 68°F | 15.4 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 51 |
Coefficient of Thermal Expansion 68-21210 to -6 power per °F (68 – 212°F) | 10.1 |
Coefficient of Thermal Expansion 68-39210 to -6 power per °F (68 – 392°F) | 11 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 11.6 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.1 |
Modulus of Elasticity in Tensionksi | 14800 |
Modulus of Rigidityksi | 5100 |
Magnetic Permeability | 1 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Fair |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Excellent |
Forgeability Rating | 95 |
Machinability Rating | 85 |
Common Fabrication Processes
Thermal Properties
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Plumbing | Cu Alloy based devices for lead-free water applications | ||
Lead-free defined by Calif. AB 1953, max .25% Pb content | |||
Lead-free,dezincification resistant alloy for potable water components | |||
valves, fittings, pumps, meters |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Forgings, Die (Hot Pressed) | ASTM | B283/B283M | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | ||
ASME | SB283 | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | |||
Rod, Bar & Shapes | Forgings | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES | |
Rod, Bar & Wire | ASTM | B967/B967M | COPPER-ZINC-TIN-BISMUTH ALLOY ROD, BAR AND WIRE |