C49360 Tin-Eco(bismuth) Wrought BRASSES Copper-Zinc-Tin Alloys (Tin Brasses) true true https://api.copper.org/alloys.xhtml/C49360
Chemical Composition
Elements
Cu(1) Pb Sn Zn Bi Si
(1) Cu + Sum of Named Elements 99.5% min.
Min (%) 1.0 19.0 0.50 2.0
Max (%) Rem 0.09 2.0 22.0 1.5 3.5
Mechanical Properties *
Form Temper Temper Code Tensile Strength
(ksi)		 Elongation
(%)		 Rockwell B scale
* Measured at room temperature, 68°F (20°C).
Rod & Bar As Hot Extruded M30 63 Typ
 17 Typ
Soft Anneal O60 63 Typ
 20 Typ
 130 Typ
Physical Properties
Melting Point - Liquidus°F 1630
Melting Point - Solidus°F 1573
Fabrication Properties
Technique Suitability
Soldering Excellent
Brazing Poor
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Spot Weld Not Recommended
Seam Weld Not Recommended
Butt Weld Not Recommended
Capacity for Being Cold Worked Poor
Capacity for Being Hot Formed Excellent
Machinability Rating 70
Common Fabrication Processes

No fabrication process properties for this alloy

Thermal Properties
Treatment Minimum* Maximum*
* Temperature is measured in Fahrenheit.
Annealing 1022 1112
Typical Uses

No information for this alloy

Applicable Specifications
Form Specific Sub-Form Application System Standard Description
Rod, Bar & Shapes ASTM B124/B124M COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES
Rod, Bar & Wire ASTM B967/B967M COPPER-ZINC-TIN-BISMUTH ALLOY ROD, BAR AND WIRE
Corrosion Properties

No Corrosion Properties Available.