C49360
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Bi | Si | |
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
Min (%) | 1.0 | 19.0 | 0.50 | 2.0 | ||
Max (%) | Rem | 0.09 | 2.0 | 22.0 | 1.5 | 3.5 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
Elongation (%) |
Rockwell B scale |
---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||
Rod & Bar | As Hot Extruded | M30 |
63 Typ |
17 Typ |
|
Soft Anneal | O60 |
63 Typ |
20 Typ |
130 Typ |
Melting Point - Liquidus°F | 1630 |
---|---|
Melting Point - Solidus°F | 1573 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Poor |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Not Recommended |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Excellent |
Machinability Rating | 70 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 1022 | 1112 |
Typical Uses
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Rod, Bar & Shapes | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES | ||
Rod, Bar & Wire | ASTM | B967/B967M | COPPER-ZINC-TIN-BISMUTH ALLOY ROD, BAR AND WIRE |