C50590
| Elements | ||||||
|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
| Min (%) | 97.0 | 0.50 | 0.05 | 0.02 | ||
| Max (%) | 0.02 | 1.5 | 0.50 | 0.40 | 0.15 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm | Fatigue Strength** (ksi) |
Proportional Limit (ksi) |
Section Size (in) |
|---|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||
| Flat Products | 1/2 Hard | H02 |
58 Typ |
53 Typ |
18 Typ |
130 Typ |
49 Typ | ||
| Hard | H04 |
74 Typ |
67 Typ |
11 Typ |
156 Typ |
28 Typ | 61 Typ | 0.009 | |
| Melting Point - Liquidus°F | 1969 |
|---|---|
| Melting Point - Solidus°F | 1904 |
| Densitylb/cu in. at 68°F | 0.321 |
| Specific Gravity | 8.9 |
| Electrical Conductivity% IACS at 68°F | 50 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 116.2 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 12300 |
| Modulus of Rigidityksi | 4600 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Gas Shielded Arc Welding | Good |
| Spot Weld | Good |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 0 |
| Machinability Rating | 20 |
Common Fabrication Processes
No fabrication process properties for this alloy
| Treatment | Minimum* | Maximum* | Time** | |
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
| Annealing | 842 | 1022 | 0.5 | |
| Hot Working Temperature | 1472 | 1742 | ||
| Stress Relief | 437 | |||
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.