C50590
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | |
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
Min (%) | 97.0 | 0.50 | 0.05 | 0.02 | ||
Max (%) | 0.02 | 1.5 | 0.50 | 0.40 | 0.15 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm | Fatigue Strength** (ksi) |
Proportional Limit (ksi) |
Section Size (in) |
---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||
Flat Products | 1/2 Hard | H02 |
58 Typ |
53 Typ |
18 Typ |
130 Typ |
49 Typ | ||
Hard | H04 |
74 Typ |
67 Typ |
11 Typ |
156 Typ |
28 Typ | 61 Typ | 0.009 |
Melting Point - Liquidus°F | 1969 |
---|---|
Melting Point - Solidus°F | 1904 |
Densitylb/cu in. at 68°F | 0.321 |
Specific Gravity | 8.9 |
Electrical Conductivity% IACS at 68°F | 50 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 116.2 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 12300 |
Modulus of Rigidityksi | 4600 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Gas Shielded Arc Welding | Good |
Spot Weld | Good |
Capacity for Being Hot Formed | Excellent |
Forgeability Rating | 0 |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | Time** | |
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Annealing | 842 | 1022 | 0.5 | |
Hot Working Temperature | 1472 | 1742 | ||
Stress Relief | 437 |
Typical Uses
Applicable Specifications
Corrosion Properties