C50705
| Elements | ||||||
|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P | |
|
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
| Min (%) | 96.5 | 1.5 | 0.10 | 0.04 | ||
| Max (%) | 0.02 | 2.0 | 0.50 | 0.40 | 0.15 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm | Fatigue Strength** (ksi) |
Proportional Limit (ksi) |
Section Size (in) |
|---|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||
| Flat Products | 1/2 Hard | H02 |
71 Typ |
67 Typ |
16 Typ |
23 Typ |
64 Typ | ||
| Extra Hard | H06 |
90 Typ |
86 Typ |
9 Typ |
193 Typ |
74 Typ | |||
| Hard | H04 |
83 Typ |
77 Typ |
13 Typ |
26 Typ |
30 Typ | 68 Typ | 0.009 | |
| Melting Point - Liquidus°F | 1976 |
|---|---|
| Melting Point - Solidus°F | 1830 |
| Densitylb/cu in. at 68°F | 0.321 |
| Specific Gravity | 8.9 |
| Electrical Conductivity% IACS at 68°F | 38 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 96.5 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 12000 |
| Modulus of Rigidityksi | 4500 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Gas Shielded Arc Welding | Good |
| Spot Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Excellent |
| Machinability Rating | 20 |
Common Fabrication Processes
No fabrication process properties for this alloy
| Treatment | Minimum* | Maximum* | Time** | |
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
| Annealing | 842 | 1022 | 0.5 | |
| Hot Working Temperature | 1408 | |||
| Stress Relief | 437 | |||
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.