C50705
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | |
(1) Cu + Sum of Named Elements 99.5% min. |
||||||
Min (%) | 96.5 | 1.5 | 0.10 | 0.04 | ||
Max (%) | 0.02 | 2.0 | 0.50 | 0.40 | 0.15 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 500 gm | Fatigue Strength** (ksi) |
Proportional Limit (ksi) |
Section Size (in) |
---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | |||||||||
Flat Products | 1/2 Hard | H02 |
71 Typ |
67 Typ |
16 Typ |
23 Typ |
64 Typ | ||
Extra Hard | H06 |
90 Typ |
86 Typ |
9 Typ |
193 Typ |
74 Typ | |||
Hard | H04 |
83 Typ |
77 Typ |
13 Typ |
26 Typ |
30 Typ | 68 Typ | 0.009 |
Melting Point - Liquidus°F | 1976 |
---|---|
Melting Point - Solidus°F | 1830 |
Densitylb/cu in. at 68°F | 0.321 |
Specific Gravity | 8.9 |
Electrical Conductivity% IACS at 68°F | 38 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 96.5 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 12000 |
Modulus of Rigidityksi | 4500 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Good |
Gas Shielded Arc Welding | Good |
Spot Weld | Good |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Excellent |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | Time** | |
---|---|---|---|---|
* Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
Annealing | 842 | 1022 | 0.5 | |
Hot Working Temperature | 1408 | |||
Stress Relief | 437 |