C52480
Elements | |||||||
---|---|---|---|---|---|---|---|
Cu(1) | Pb | Sn | Zn | Fe | P | Ni | |
(1) Cu + Sum of Named Elements 99.5% min. |
|||||||
Min (%) | 9.0 | 0.05 | 0.01 | 0.05 | |||
Max (%) | Rem | 0.05 | 11.0 | 0.30 | 0.20 | 0.35 | 0.20 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||
Flat Products | 1/2 Hard | H02 |
110 Typ |
103 Typ |
20 Typ |
1/4 Hard | H01 |
92 Typ |
70 Typ |
30 Typ |
|
Extra Hard | H06 |
130 Typ |
125 Typ |
6 Typ |
|
Extra Spring | H10 |
146 Typ |
142 Typ |
2 Typ |
|
Hard | H04 |
123 Typ |
119 Typ |
10 Typ |
|
Nominal Grain Size 0.015 mm | OS015 |
75 Typ |
38 Typ |
55 Typ |
|
Spring | H08 |
140 Typ |
137 Typ |
2 Typ |
Melting Point - Liquidus°F | 1830 |
---|---|
Melting Point - Solidus°F | 1550 |
Densitylb/cu in. at 68°F | 0.317 |
Specific Gravity | 8.78 |
Electrical Conductivity% IACS at 68°F | 11 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 29 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10.2 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 16000 |
Modulus of Rigidityksi | 6000 |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Fair |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Fair |
Spot Weld | Good |
Seam Weld | Fair |
Butt Weld | Excellent |
Capacity for Being Cold Worked | Good |
Machinability Rating | 20 |
Common Fabrication Processes
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 700 | 1250 |
Typical Uses
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Strip | ASTM | B888/B88M | COPPER ALLOY STRIP FOR USE IN MANUFACTURE OF ELECTRICAL CONNECTORS OR SPRING CONTACTS |
Corrosion Properties