C61000
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1,2) | Pb | Zn | Fe | Al | Si | |
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. |
||||||
Min (%) | 6.0 | |||||
Max (%) | Rem | 0.02 | 0.20 | 0.50 | 8.5 | 0.10 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Torsion Modulus (ksi) |
Section Size (in) |
---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||||
Plate | Hard | H04 |
60 Typ |
27 Typ |
30 Typ |
85 Typ |
1 | |
Hard | H04 |
65 Typ |
24 Typ |
30 Typ |
85 Typ |
0.5 | ||
Soft Anneal | O60 |
52 Typ |
17 Typ |
45 Typ |
60 Typ |
1 | ||
Rod | Hard | H04 |
80 Typ |
25 Typ |
6.4 Typ | 1 | ||
Soft Anneal | O60 |
70 Typ |
30 Typ |
65 Typ |
1 | |||
Sheet | Hard | H04 |
65 Typ |
24 Typ |
30 Typ |
85 Typ |
0.5 | |
Hard | H04 |
60 Typ |
27 Typ |
30 Typ |
85 Typ |
1 | ||
Soft Anneal | O60 |
52 Typ |
17 Typ |
45 Typ |
60 Typ |
1 | ||
Strip | Hard | H04 |
65 Typ |
24 Typ |
30 Typ |
85 Typ |
0.5 | |
Hard | H04 |
60 Typ |
27 Typ |
30 Typ |
85 Typ |
1 | ||
Soft Anneal | O60 |
52 Typ |
17 Typ |
45 Typ |
60 Typ |
1 |
Melting Point - Liquidus°F | 1905 |
---|---|
Densitylb/cu in. at 68°F | 0.281 |
Specific Gravity | 7.78 |
Electrical Conductivity% IACS at 68°F | 15 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 40 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.9 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 17000 |
Modulus of Rigidityksi | 6400 |
Technique | Suitability |
---|---|
Soldering | Fair |
Brazing | Not Recommended |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Good |
Spot Weld | Good |
Seam Weld | Fair |
Butt Weld | Good |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Good |
Forgeability Rating | 70 |
Machinability Rating | 20 |
Common Fabrication Processes
- Blanking
- Drawing
- Forming and Bending
- Heading and Roll Threading
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 1100 | 1250 | ||
Hot Working Temperature | 1400 | 1600 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Architecture | Decorative Applications | Appearance | Appearance |
Decorative Applications | Appearance | Gold Color | |
Decorative Applications | Mechanical Properties | Moderate Strength | |
Fasteners | Bolts | Forming Characteristics | Formability |
Bolts | Mechanical Properties | Moderate Strength | |
Industrial | Overlay on Steel for Wearing Surface | Friction & Wear Properties | Wear Resistance |
Overlay on Steel for Wearing Surface | Mechanical Properties | Moderate Strength | |
Overlay on Steel for Wearing Surface | Welding Characteristics | Weldability | |
Pump Parts | Forming Characteristics | Formability | |
Pump Parts | Friction & Wear Properties | Wear Resistance | |
Pump Parts | Mechanical Properties | Moderate Strength | |
Pump Parts | Mechanical Properties | Toughness | |
Shafts | Forming Characteristics | Formability | |
Shafts | Mechanical Properties | Ductility | |
Shafts | Mechanical Properties | Moderate Strength | |
Tie Rods | Friction & Wear Properties | Wear Resistance | |
Tie Rods | Mechanical Properties | Moderate Strength | |
Tie Rods | Welding Characteristics | Weldability | |
Welding Wire | Welding Characteristics | Weld Alloy - c61300 |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Bar | FEDERAL | QQ-C-450 | COPPER-ALUMINUM ALLOY (ALUMINUM BRONZE, PLATE, SHEET, STRIP, AND BAR) | ||
Electrode | Welding | MILITARY | MIL-E-23765/3 | ELECTRODES, WELDING, BARE, COPPER AND COPPER ALLOY | |
AWS | A5.7 | COPPER AND COPPER ALLOY BARS, WELDING RODS | |||
Plate | FEDERAL | QQ-C-450 | COPPER-ALUMINUM ALLOY (ALUMINUM BRONZE, PLATE, SHEET, STRIP, AND BAR) | ||
Sheet | FEDERAL | QQ-C-450 | COPPER-ALUMINUM ALLOY (ALUMINUM BRONZE, PLATE, SHEET, STRIP, AND BAR) | ||
Strip | FEDERAL | QQ-C-450 | COPPER-ALUMINUM ALLOY (ALUMINUM BRONZE, PLATE, SHEET, STRIP, AND BAR) |
Corrosion Properties