C63200
Elements | |||||||
---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Fe(3) | Ni(4,5) | Al | Mn | Si | |
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. (3) Fe content shall not exceed Ni content. (4) Ni value includes Co. (5) Fe content shall not exceed Ni content. |
|||||||
Min (%) | 3.5 | 4.0 | 8.7 | 1.2 | |||
Max (%) | Rem | 0.02 | 4.3 | 4.8 | 9.5 | 2.0 | 0.10 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Torsion Modulus (ksi) |
Izod (ft-lbs) |
Compressive Strength .001 in. set/in. (ksi) |
Reduction of Area (%) |
Section Size (in) |
---|---|---|---|---|---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | |||||||||||
Forgings | Light Anneal | O50 |
100 Typ |
45 Typ |
22 Typ |
92 Typ |
5 | ||||
Plate | Light Anneal | O50 |
95 Typ |
47 Typ |
22 Typ |
89 Typ |
6.4 Typ | 17 Typ | 110 Typ | 18 Typ | 0.5 |
Light Anneal | O50 |
100 Typ |
50 Typ |
20 Typ |
92 Typ |
0.25 | |||||
Light Anneal | O50 |
90 Typ |
45 Typ |
25 Typ |
85 Typ |
1 | |||||
Rod | Light Anneal | O50 |
103 Typ |
52 Typ |
24 Typ |
94 Typ |
2 | ||||
Light Anneal | O50 |
105 Typ |
53 Typ |
22 Typ |
96 Typ |
1 | |||||
Light Anneal | O50 |
102 Typ |
51 Typ |
24 Typ |
93 Typ |
3 |
Melting Point - Liquidus°F | 1940 |
---|---|
Melting Point - Solidus°F | 1905 |
Densitylb/cu in. at 68°F | 0.276 |
Specific Gravity | 7.64 |
Electrical Conductivity% IACS at 68°F | 7 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 20 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.105 |
Modulus of Elasticity in Tensionksi | 17000 |
Modulus of Rigidityksi | 6400 |
Technique | Suitability |
---|---|
Soldering | Fair |
Brazing | Fair |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Excellent |
Coated Metal Arc Welding | Good |
Spot Weld | Good |
Seam Weld | Fair |
Butt Weld | Good |
Capacity for Being Cold Worked | Fair |
Capacity for Being Hot Formed | Good |
Forgeability Rating | 70 |
Machinability Rating | 30 |
Common Fabrication Processes
- Hot Forming
- Welding
Treatment | Minimum* | Maximum* | ||
---|---|---|---|---|
* Temperature is measured in Fahrenheit. | ||||
Annealing | 1150 | 1300 | ||
Hot Working Temperature | 1500 | 1650 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Fasteners | Bolting | Corrosion Resistance | Corrosion Resistance |
Bolting | Corrosion Resistance | Corrosion Resistance to Chemicals | |
Bolting | Corrosion Resistance | Corrosion Resistance to Non Oxidizing Acids | |
Bolting | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
Bolting | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Bolting | Mechanical Properties | High Strength | |
Fasteners, Sea Water | Corrosion Resistance | Corrosion Resistance | |
Fasteners, Sea Water | Corrosion Resistance | Stress Corrosion Cracking Resistance | |
Fasteners, Sea Water | Friction & Wear Properties | Wear Resistance | |
Fasteners, Sea Water | Mechanical Properties | High Strength | |
Nuts | Corrosion Resistance | Corrosion Resistance | |
Nuts | Corrosion Resistance | Corrosion Resistance to Chemicals | |
Nuts | Corrosion Resistance | Corrosion Resistance to Non Oxidizing Acids | |
Nuts | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
Nuts | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Nuts | Mechanical Properties | High Strength | |
Industrial | Bearing Cages | Friction & Wear Properties | Wear Resistance |
Bearing Cages | Mechanical Properties | Fatigue Resistance | |
Bearing Cages | Mechanical Properties | High Strength | |
Bearing Cages | Softening Resistance | Softening Resistant to 600 F. | |
Bushings | Friction & Wear Properties | Wear Resistance | |
Bushings | Mechanical Properties | Fatigue Resistance | |
Bushings | Softening Resistance | Softening Resistant to 600 F. | |
Cams | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Cams | Friction & Wear Properties | Wear Resistance | |
Cams | Mechanical Properties | Fatigue Resistance | |
Cams | Mechanical Properties | High Strength | |
Cams | Softening Resistance | Softening Resistant to 600 F. | |
Sea Water Pump Bodies | Corrosion Resistance | Corrosion Resistance | |
Sea Water Pump Bodies | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Sea Water Pump Bodies | Corrosion Resistance | Stress Corrosion Cracking Resistance | |
Sea Water Pump Bodies | Friction & Wear Properties | Wear Resistance | |
Sea Water Pump Bodies | Mechanical Properties | High Strength | |
Sea Water Valves | Corrosion Resistance | Corrosion Resistance | |
Sea Water Valves | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Sea Water Valves | Corrosion Resistance | Stress Corrosion Crack Resistance | |
Sea Water Valves | Friction & Wear Properties | Wear Resistance | |
Sea Water Valves | Mechanical Properties | High Strength | |
Shafts | Corrosion Resistance | Corrosion Resistance | |
Shafts | Corrosion Resistance | Corrosion Resistance to Chemicals | |
Shafts | Corrosion Resistance | Corrosion Resistance to Non Oxidizing Acids | |
Shafts | Corrosion Resistance | Corrosion Resistance to Numerous Environments | |
Shafts | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Shafts | Mechanical Properties | High Strength | |
Sleeve Bearings | Friction & Wear Properties | Wear Resistance | |
Sleeve Bearings | Mechanical Properties | Fatigue Resistance | |
Sleeve Bearings | Mechanical Properties | High Strength | |
Sleeve Bearings | Softening Resistance | Softening Resistant to 600 F. | |
Valve Stems | Corrosion Resistance | Corrosion Resistance to Non-Oxidizing Mineral Acids | |
Valve Stems | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Valve Stems | Mechanical Properties | Fatigue Resistance | |
Valve Stems | Mechanical Properties | High Strength | |
Valve Stems | Welding Characteristics | Weldable - Gas shielded and Metal-Arc | |
Marine | Drive Shafts, Marine Service | Corrosion Resistance | Corrosion Resistance |
Drive Shafts, Marine Service | Corrosion Resistance | Corrosion Resistance to Salt Water | |
Drive Shafts, Marine Service | Corrosion Resistance | Stress Corrosion Cracking Resistance | |
Drive Shafts, Marine Service | Friction & Wear Properties | Wear Resistance | |
Drive Shafts, Marine Service | Mechanical Properties | Moderate Strength |
Form | Specific Sub-Form | Application | System | Standard | Description |
---|---|---|---|---|---|
Bar | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES | ||
Electrode | Welding | MILITARY | MIL-E-23765/3 | ELECTRODES, WELDING, BARE, COPPER AND COPPER ALLOY | |
Welding | AWS | A5.6 | COPPER AND COPPER ALLOY COVERED ELECTRODES | ||
Forgings, Die (Hot Pressed) | ASME | SB283 | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | ||
ASTM | B283/B283M | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | |||
Plate & Sheet | for Pressure Vessels, Condensers & Heat Exchangers | ASTM | B171/B171M | COPPER ALLOY CONDENSER TUBE PLATES | |
for Pressure Vessels, Condensers & Heat Exchangers | ASME | SB171 | COPPER ALLOY CONDENSER TUBE PLATES | ||
Rod | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES | ||
Rod, Bar & Shapes | Aluminum Bronze | ASTM | B150/B150M | ALUMINUM BRONZE ROD, BAR AND SHAPES | |
Aluminum Bronze | ASME | SB150 | ALUMINUM BRONZE ROD, BAR, AND SHAPES | ||
Shapes | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES |
Corrosion Properties