C64200
| Elements | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1,2) | Pb | Sn | Zn | Fe | Ni(3) | Al | As | Mn | Si | |
|
(1) Cu value includes Ag. (2) Cu + Sum of Named Elements 99.5% min. (3) Ni value includes Co. |
||||||||||
| Min (%) | 6.3 | 1.5 | ||||||||
| Max (%) | Rem | 0.05 | 0.20 | 0.50 | 0.30 | 0.25 | 7.6 | 0.09 | 0.10 | 2.2 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Shear Strength (ksi) |
Fatigue Strength** (ksi) |
Section Size (in) |
Cold Work (%) |
|---|---|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | ||||||||||
| Bar | As Hot Extruded | M30 |
75 Typ |
35 Typ |
32 Typ |
77 Typ |
0.75 | |||
| Forgings | As Hot Forged - Air Cooled | M10 |
79 Typ |
38 Typ |
30 Typ |
78 Typ |
2 | |||
| Rod | As Hot Extruded | M30 |
75 Typ |
35 Typ |
32 Typ |
77 Typ |
0.75 | |||
| Hard | H04 |
102 Typ |
68 Typ |
22 Typ |
94 Typ |
59 Typ |
50 Typ | 0.75 | 15 | |
| Hard | H04 |
93 Typ |
60 Typ |
26 Typ |
90 Typ |
1.5 | 10 | |||
| Light Anneal | O50 |
90 Typ |
55 Typ |
28 Typ |
89 Typ |
0.75 | ||||
| Light Anneal | O50 |
92 Typ |
58 Typ |
22 Typ |
98 Typ |
0.5 | ||||
| Melting Point - Liquidus°F | 1840 |
|---|---|
| Melting Point - Solidus°F | 1800 |
| Densitylb/cu in. at 68°F | 0.278 |
| Specific Gravity | 7.69 |
| Electrical Conductivity% IACS at 68°F | 8 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 26 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 16000 |
| Modulus of Rigidityksi | 6000 |
| Technique | Suitability |
|---|---|
| Soldering | Not Recommended |
| Brazing | Fair |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Fair |
| Spot Weld | Fair |
| Seam Weld | Fair |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 80 |
| Machinability Rating | 60 |
Common Fabrication Processes
- Forging
- Hot Forming
- Machining
| Treatment | Minimum* | Maximum* | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. | ||||
| Annealing | 1100 | 1300 | ||
| Hot Working Temperature | 1300 | 1600 | ||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Automotive | Valve Guides, Automobile Engine | Corrosion Resistance | Corrosion Resistance |
| Valve Guides, Automobile Engine | Friction & Wear Properties | Galling Resistance | |
| Valve Guides, Automobile Engine | Friction & Wear Properties | Wear Resistance | |
| Valve Guides, Automobile Engine | Mechanical Properties | High Strength | |
| Electrical | Pole Line Hardware | Conductivity (Electrical) | Electrical Conductivity |
| Pole Line Hardware | Corrosion Resistance | Corrosion Resistance | |
| Pole Line Hardware | Friction & Wear Properties | Wear Resistance | |
| Pole Line Hardware | Machining Characteristics | Machinability | |
| Pole Line Hardware | Magnetic Properties | Non-Magnetic | |
| Fasteners | Bolts | Corrosion Resistance | Corrosion Resistance |
| Bolts | Machining Properties | Machinability, Good | |
| Bolts | Mechanical Properties | High Strength | |
| Nuts | Corrosion Resistance | Corrosion Resistance | |
| Nuts | Forming Characteristics | Formability | |
| Nuts | Machining Properties | Machinability, Good | |
| Nuts | Mechanical Properties | High Strength | |
| Industrial | Cams | Corrosion Resistance | Corrosion Resistance |
| Cams | Friction & Wear Properties | Wear Resistance | |
| Cams | Machining Properties | Machinability, Good | |
| Cams | Mechanical Properties | High Strength | |
| Gears | Corrosion Resistance | Corrosion Resistance | |
| Gears | Friction & Wear Properties | Wear Resistance | |
| Gears | Machining Characteristics | Machinability | |
| Gears | Magnetic Properties | Non-Magnetic | |
| Valve Bodies | Corrosion Resistance | Corrosion Resistance | |
| Valve Bodies | Forming Characteristics | Formability | |
| Valve Bodies | Machining Properties | Machinability, Good | |
| Valve Bodies | Mechanical Properties | High Strength | |
| Valve Components | Corrosion Resistance | Corrosion Resistance | |
| Valve Components | Forming Characteristics | Formability | |
| Valve Components | Machining Properties | Machinability, Good | |
| Valve Components | Mechanical Properties | High Strength | |
| Valve Stems | Corrosion Resistance | Corrosion Resistance | |
| Valve Stems | Friction & Wear Properties | Wear Resistance | |
| Valve Stems | Machining Characteristics | Machinability | |
| Valve Stems | Magnetic Properties | Non-Magnetic | |
| Marine | Hardware | Corrosion Resistance | Corrosion Resistance |
| Hardware | Forming Characteristics | Formability | |
| Hardware | Machining Properties | Machinability, Good | |
| Hardware | Mechanical Properties | High Strength |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| Bar | AMS | 4631 | ALUMINUM BRONZE RODS, BARS, AND FORGINGS | ||
| Bolts | ASTM | F468 | NONFERROUS BOLTS, HEX CAP SCREWS, AND STUDS FOR GENERAL USE | ||
| Die | Forgings | AMS | 4631 | ALUMINUM BRONZE RODS, BARS, AND FORGINGS | |
| Forgings, Die (Hot Pressed) | ASME | SB283 | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | ||
| ASTM | B283/B283M | COPPER AND COPPER ALLOY DIE FORGINGS (HOT PRESSED) | |||
| Nuts | ASTM | F467 | NONFERROUS NUTS FOR GENERAL USE | ||
| Rod | SAE | J463 | WROUGHT COPPER AND COPPER ALLOYS | ||
| SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |||
| AMS | 4631 | ALUMINUM BRONZE RODS, BARS, AND FORGINGS | |||
| Rod, Bar & Shapes | Aluminum Bronze | ASME | SB150 | ALUMINUM BRONZE ROD, BAR, AND SHAPES | |
| Aluminum Bronze | ASTM | B150/B150M | ALUMINUM BRONZE ROD, BAR AND SHAPES | ||
| Forgings | ASTM | B124/B124M | COPPER AND COPPER-ALLOY FORGING ROD, BAR AND SHAPES | ||
| Screws | ASTM | F468 | NONFERROUS BOLTS, HEX CAP SCREWS, AND STUDS FOR GENERAL USE | ||
| Studs | ASTM | F468 | NONFERROUS BOLTS, HEX CAP SCREWS, AND STUDS FOR GENERAL USE |
| Environmental Category | Specific Environment | Resistance Level | Corrosion notes |
|---|---|---|---|
| Atmosphere | Atmosphere, Industrial | Not Recommended | Affected by pollutants and other environmental factors. Hydrogen sulfide causes rapid tarnishing. |