C64751
| Elements | ||||||
|---|---|---|---|---|---|---|
| Cu(1) | Sn | Zn | P | Ni | Si | |
|
(1) Cu + Sum of Named Elements, 99.92% min. |
||||||
| Min (%) | 0.10 | 2.5 | 0.50 | |||
| Max (%) | Rem | 0.40 | 0.10 | 0.02 | 3.1 | 0.9 |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.2% Offset (ksi) |
Elongation (%) |
Vickers Hardness, 3000 gm |
|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). | ||||||
| Strip | 1/2 Hard | H02 |
101 Min 108 Typ 116 Max |
88 Min 97 Typ 107 Max |
8 Min |
228 Min |
| Extra Hard | H06 |
116 Min 123 Typ 131 Max |
110 Min 119 Typ 127 Max |
1 Min |
255 Min |
|
| Hard | H04 |
110 Min 119 Typ 126 Max |
104 Min 113 Typ 121 Max |
2 Min |
245 Min |
|
| Melting Point - Liquidus°F | 1967 |
|---|---|
| Melting Point - Solidus°F | 1922 |
| Densitylb/cu in. at 68°F | 0.32 |
| Specific Gravity | 8.89 |
| Electrical Conductivity% IACS at 68°F | 34 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 95 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.61 |
| Modulus of Elasticity in Tensionksi | 19000 |
| Poisson's Ratio | 0.33 |
| Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |
| Spot Weld | Excellent |
| Seam Weld | Excellent |
| Butt Weld | Excellent |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Fair |
Common Fabrication Processes
No fabrication process properties for this alloy
Thermal Properties
No thermal properties for this alloy
Typical Uses
No information for this alloy
Applicable Specifications
No applicable specifications for this alloy
Corrosion Properties
No Corrosion Properties Available.